Graphene-Confined Growth of Few-Layer PtSe2 via One-Step Selenization

Platinum diselenide (PtSe${}_2$), a member of the transition metal dichalcogenide (TMD) family, is a promising material for next-generation electronic and optoelectronic applications due to its thickness-dependent properties, transitioning from semimetallic in bulk to semiconducting behavior at the few-layer limit. However, the scalable fabrication of large-area ultrathin PtSe${}_2$ films remains challenging, as conventional selenization of pre-deposited Pt layers often leads to undesired three-dimensional clustered growth. This work explores a novel strategy for promoting two-dimensional growth of PtSe${}_2$ by employing a graphene-mediated confinement approach. The method involves coating a Pt layer with graphene oxide (GO), followed by annealing in a selenium atmosphere, which results in the simultaneous formation of PtSe${}_2$ and the reduction of GO to graphene. The graphene overlayer acts as a physical confinement layer, suppressing vertical growth and enabling the synthesis of graphene-confined PtSe${}_2$ heterostructures on centimetre-scale substrates and promoting lateral connectivity of PtSe${}_2$ regions observed by STEM. Scanning transmission electron microscopy (STEM), including temperature-resolved in situ atomic-resolution measurements, was used to investigate the influence of selenization temperature on the growth mechanism and structural evolution of PtSe${}_2$ films. The results show that graphene confinement stabilizes lateral growth and promotes the formation of few-layer films with improved structural ordering. Beyond PtSe${}_2$, this graphene-assisted approach provides a general strategy for fabricating and stabilizing ultrathin TMD layers, including those prone to environmental degradation, providing a new outlook for enabling detailed studies of their intrinsic properties.